Standard Specification for Amorphous Magnetic Core Alloys, Semi-Processed Types
STANDARD published on 1.11.2024
Why Redline?
A PDF redline is a quick and easy way to compare all of the changes between the current, active standard and the previous version.
With a redline you'll immediately see:
Save Time and Trouble!
With a Redline you no longer have to spend time trying to determine what has changed in the new standard! Redlines save you time and ensure you see what the changes are to the standard.
Price
When you select the "Active + Redline" option you get both documents! Best of all, the cost of an Active + Redline is only slightly more than buying the Active Standard by itself.
Designation standards: ASTM A901-24
Publication date standards: 1.11.2024
The number of pages: 5
Approximate weight : 15 g (0.03 lbs)
Country: American technical standard
Category: Technical standards ASTM
This specification covers the requirements to which flat-cast, amorphous, semi-processed, iron-base magnetic core alloys must conform. These alloys shall be produced by a rapid-quenching, direct-casting process, resulting in metals with noncrystalline structure. The alloys shall be made to meet specified maximum core-loss values and shall be intended primarily for commercial power frequency applications. Desirable core-loss and permeability characteristics shall be developed by further heat treatment in a magnetic field. Amorphous magnetic core alloys are normally composed of iron with small amounts of alloying elements such as boron and silicon. There are no specific chemical requirements in this specification. Material produced to this specification shall conform to the required physical and mechanical properties such as density, ductility, thermal expansion, thermal conductivity, volume resistivity, lamination factor, surface, edge, and pinholes. The alloy shall also conform to the magnetic property requirements such as DC induction, DC coercive field strength, DC residual induction, core loss, and specific exciting power.
Keywords:
amorphous, coercive field strength, core loss, induction, residual induction, specific exciting power,, ICS Number Code 29.030 (Magnetic materials),29.100.10 (Magnetic components)