Standard Specification for Steel Sheet, Zinc-5 % Aluminum Alloy-Coated by the Hot-Dip Process
STANDARD published on 1.10.2023
Why Redline?
A PDF redline is a quick and easy way to compare all of the changes between the current, active standard and the previous version.
With a redline you'll immediately see:
Save Time and Trouble!
With a Redline you no longer have to spend time trying to determine what has changed in the new standard! Redlines save you time and ensure you see what the changes are to the standard.
Price
When you select the "Active + Redline" option you get both documents! Best of all, the cost of an Active + Redline is only slightly more than buying the Active Standard by itself.
Designation standards: ASTM A875/A875M-23
Publication date standards: 1.10.2023
The number of pages: 12
Approximate weight : 36 g (0.08 lbs)
Country: American technical standard
Category: Technical standards ASTM
This specification covers steel sheet, in coils and cut lengths, metallic-coated by the hot-dip process, with zinc-aluminum alloy coating. The coating is produced as two types: zinc-aluminum-mischmetal alloy (Type I) and zinc-aluminum-magnesium alloy (Type II), and in two coating structures. Coated sheet is produced in several coating designations (coating weight [mass]). Material is classified in terms of the base metal and in terms of the coating. Base metal material classification is as follows: commercial steel (CS Types A, B, and C), forming steel (FS Types A and B), deep drawing steel (DDS), extra deep drawing steel (EDDS), structural steel (SS), high-strength low-alloy steel (HSLAS), and high-strength low-alloy steel with improved formability (HSLAS-F). Structural steel and high strength low alloy steel are available in several grades based on mechanical properties. Structural steel grade 50 [340] is available in three classes based on tensile strength. Heat analysis of the base metal for CS , FS, DDS, and EDDS shall conform to the chemical composition requirements in carbon, manganese, phosphorus, sulfur, aluminum, copper, nickel, chromium, molybdenum, vanadium, titanium, nitrogen, and boron and chemical composition in carbon, manganese, phosphorus, sulfur, copper, nickel, chromium, molybdenum, vanadium, titanium, nitrogen for SS, HSLAS, and HSLAS-F. Structural steel shall conform to the required yield strength, tensile strength, and elongation. Coating shall conform to the coating weight according to triple-spot test and single-spot test and shall be capable of bending without flaking.
Keywords:
coatings, metallic, steel sheet, zinc alloy coated, steel sheet, zinc coated, zinc alloys, zinc-coated steel, zinc-5 % aluminum-0.1 % magnesium alloy-coated steel, zinc-5 % aluminum alloy-coated steel, zinc-5 % aluminum-mischmetal alloy-coated steel,, ICS Number Code 77.140.50 (Flat steel products and semi-products)