API TR 934-FPART2
Literature Review of Fracture Mechanics-based Experimental Data for Internal Hydrogen-assisted Cracking of Vanadium-modified 21/4Cr-Mo Steel, First Edition
Translate name
STANDARD published on 1.8.2017
The information about the standard:
Designation standards: API TR 934-FPART2
Publication date standards: 1.8.2017
SKU: NS-1251059
The number of pages: 46
Approximate weight : 138 g (0.30 lbs)
Country: American technical standard
Category: Technical standards API
Annotation of standard text API TR 934-FPART2 :
This technical report documents a critical assessment of the existing literature on IHAC of V-modified Cr-Mo steels for use in interpreting the results of the present laboratory work, so as to establish a definitive characterization of the H cracking resistance of this steel class.
Since these modern Cr-Mo-V steels are of relatively high purity, and thus retain a low FATT after laboratory simulation of in-service temper embrittlement, the data base for 21Cr-1Mo shown in Figure 1 provides a context for assessment of the IHAC performance of V-modified grades. Hydrogen cracking of less-pure V-modified Cr-Mo steels was not considered in this review.
The content of this technical report is chronologically organized into initial and more modern works, as justified by improvement in test execution, data analysis, and reporting, as well as the evolution from laboratory to commercial scale heats of Cr-Mo-V. See more
We recommend:
Technical standards updating
Do you want to make sure you use only the valid technical standards?
We can offer you a solution which will provide you a monthly overview concerning the updating of standards which you use.
Would you like to know more? Look at this page.