ASTM A193/A193M-10
Standard Specification for Alloy-Steel and Stainless Steel Bolting Materials for High Temperature or High Pressure Service and Other Special Purpose Applications
STANDARD published on 1.5.2010
The information about the standard:
Designation standards: ASTM A193/A193M-10
Note: WITHDRAWN
Publication date standards: 1.5.2010
SKU: NS-1504
The number of pages: 12
Approximate weight : 36 g (0.08 lbs)
Country: American technical standard
Category: Technical standards ASTM
Annotation of standard text ASTM A193/A193M-10 :
Keywords:
hardness, heat treatment, Alloy steel bolting materials--specifications, High-temperature service applications--steel bolting applications, Stainless steel bolting materials--specifications, Stainless steel fittings--specifications, Steel fittings--specifications, Steel flanges--specifications, Steel valves--specifications, ICS Number Code 21.060.01 (Fasteners in general), 77.080.20 (Steels)
Additional information
| 1. Scope | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|
1.1 This specification covers alloy and stainless steel bolting material for pressure vessels, valves, flanges, and fittings for high temperature or high pressure service, or other special purpose applications. The term bolting material as used in this specification covers bars, bolts, screws, studs, stud bolts, and wire. Bars and wire shall be hot-wrought. The material may be further processed by centerless grinding or by cold drawing. Austenitic stainless steel may be carbide solution treated or carbide solution treated and strain-hardened. When strain hardened austenitic steel is ordered, the purchaser should take special care to ensure that Appendix X1 is thoroughly understood. 1.2 Several grades are covered, including ferritic steels and austenitic stainless steels designated B5, B8, and so forth. Selection will depend upon design, service conditions, mechanical properties, and high temperature characteristics. 1.3 The following referenced general requirements are indispensable for application of this specification: Specification A962/A962M. Note 1—The committee formulating this specification has included fifteen steel types that have been rather extensively used for the present purpose. Other compositions will be considered for inclusion by the committee from time to time as the need becomes apparent. Note 2—For grades of alloy-steel bolting material suitable for use at the lower range of high temperature applications, reference should be made to Specification A354. Note 3—For grades of alloy-steel bolting material suitable for use in low temperature applications, reference should be made to Specification A320/A320M. 1.4 Nuts for use with this bolting material are covered in Section 14. 1.5 Supplementary Requirements S1 through S14 are provided for use when additional tests or inspection are desired. These shall apply only when specified in the purchase order. 1.6 This specification is expressed in both inch-pound units and in SI units. However, unless the order specifies the applicable M specification designation (SI units), the material shall be furnished to inch-pound units. 1.7 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system may not be exact equivalents; therefore, each system shall be used independently of the other. Combining values from the two systems may result in non-conformance with the standard. Within the text, the SI units are shown in brackets. |
||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
| 2. Referenced Documents | ||||||||||||||||||||||||||||||||||||||||||||||||||||||||||
|
We recommend:
Updating of laws
Do you want to be sure about the validity of used regulations?
We offer you a solution so that you could use valid and updated legislative regulations.
Would you like to get more information? Look at this page.