ASTM A225/A225M-93(1999)
Standard Specification for Pressure Vessel Plates, Alloy Steel, Manganese-Vanadium-Nickel
STANDARD published on 10.9.1999
The information about the standard:
Designation standards: ASTM A225/A225M-93(1999)
Note: WITHDRAWN
Publication date standards: 10.9.1999
SKU: NS-1646
The number of pages: 2
Approximate weight : 6 g (0.01 lbs)
Country: American technical standard
Category: Technical standards ASTM
Annotation of standard text ASTM A225/A225M-93(1999) :
Keywords:
Manganese-vanadium alloys, Pressure vessel steel materials-plates, Steel plate-manganese alloy, plates-Mn-V-Ni alloy steel, for welded/layered pressure vessels, spec, ICS Number Code 77.140.30 (Steels for pressure purposes)
Additional information
| 1. Scope | ||||||||
|
1.1 This specification covers manganese-vanadium-nickel alloy steel plates intended primarily for welded layered pressure vessels. 1.2 Material under this specification is available in two grades having different strength levels as follows: Tensile Strength, Grade ksi [Mpa] C 105-135 [725-930] D 3 in.[75 mm] and under 80-105 [550-725] Over 3 in.[75 mm] 75-100 [515-690]1.3 The maximum thickness of plates is limited only by the capacity of the chemical composition to meet the specified mechanical property requirements; however, current mill practice normally limits Grade C to 0.58 in. [15 mm] maximum and Grade D to 6 in. [150 mm] maximum. 1.4 The values stated in either inch-pound units or SI units are to be regarded separately as standard. Within the text, the SI units are shown in brackets. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the specification. |
||||||||
| 2. Referenced Documents | ||||||||
|