ASTM A587-96(2012)
Standard Specification for Electric-Resistance-Welded Low-Carbon Steel Pipe for the Chemical Industry
STANDARD published on 1.3.2012
The information about the standard:
Designation standards: ASTM A587-96(2012)
Note: WITHDRAWN
Publication date standards: 1.3.2012
SKU: NS-3244
The number of pages: 6
Approximate weight : 18 g (0.04 lbs)
Country: American technical standard
Category: Technical standards ASTM
The category - similar standards:
Annotation of standard text ASTM A587-96(2012) :
Keywords:
ICS Number Code 23.040.10 (Iron and steel pipes)
Additional information
| 1. Scope | |||||||
|
1.1 This specification2 covers electric-resistance-welded low-carbon steel pipe intended for use as process lines. 1.2 Pipe ordered under this specification shall be suitable for severe forming operations involving flanging in all sizes and bending to close radii up to and including NPS 4. 1.3 This specification covers NPS 1/2 through 10, plus additional sizes. The corresponding outside diameters and wall thicknesses for NPS 1/2 through 10 are listed in NPS |
Outside Diameter |
Wall Thickness |
|||||
|
Min |
Nom |
Max |
Min |
Nom |
Max |
||
|
|
Inches |
||||||
|
— |
0.8125 ± 0.004 |
0.095 |
0.103 |
0.111 |
0.129 |
0.140 |
0.151 |
|
1/2 |
0.840 ± 0.006 |
0.095 |
0.103 |
0.111 |
0.125 |
0.140 |
0.151 |
|
3/4 |
1.050 ±0.006 |
0.099 |
0.108 |
0.117 |
0.135 |
0.147 |
0.159 |
|
— |
1.0625 ± 0.006 |
0.099 |
0.108 |
0.117 |
0.135 |
0.147 |
0.159 |
|
— |
1.3125 ± 0.006 |
0.116 |
0.126 |
0.136 |
0.157 |
0.171 |
0.185 |
|
1 |
1.315 ± 0.006 |
0.116 |
0.126 |
0.136 |
0.157 |
0.171 |
0.185 |
|
11/4 |
1.660 ± 0.007 |
0.121 |
0.132 |
0.143 |
0.167 |
0.182 |
0.197 |
|
— |
1.875 ± 0.008 |
0.127 |
0.138 |
0.149 |
0.175 |
0.190 |
0.205 |
|
11/2 |
1.900 ± 0.008 |
0.127 |
0.158 |
0.149 |
0.175 |
0.190 |
0.205 |
|
2 |
2.375 ± 0.010 |
0.135 |
0.147 |
0.159 |
0.191 |
0.208 |
0.225 |
|
3 |
3.500 ± 0.015 |
0.189 |
0.206 |
0.223 |
0.262 |
0.286 |
0.310 |
|
4 |
4.500 ± 0.017 |
0.207 |
0.226 |
0.245 |
0.295 |
0.322 |
0.349 |
|
6 |
6.625 ± .030 |
0.245 |
0.267 |
0.289 |
0.378 |
0.412 |
0.446 |
|
8 |
8.625 ± .040 |
0.282 |
0.308 |
0.334 |
0.438 |
0.478 |
0.518 |
|
10 |
10.750 ± .050 |
0.319 |
0.348 |
0.377 |
0.520 |
0.567 |
0.614 |
|
|
Millimetres |
||||||
|
— |
20.64 ± 0.10 |
2.41 |
2.62 |
2.82 |
3.28 |
3.56 |
3.84 |
|
1/2 |
21.30 ± 0.15 |
2.41 |
2.62 |
2.82 |
3.28 |
3.56 |
3.84 |
|
3/4 |
26.70 ± 0.15 |
2.51 |
2.74 |
2.97 |
3.43 |
3.73 |
4.04 |
|
— |
26.99 ± 0.15 |
2.51 |
2.74 |
2.97 |
3.43 |
3.73 |
4.04 |
|
— |
33.34 ± 0.15 |
2.95 |
3.20 |
3.45 |
3.99 |
4.34 |
4.70 |
|
1 |
33.40 ± 0.15 |
2.95 |
3.20 |
3.45 |
3.99 |
4.34 |
4.70 |
|
11/4 |
42.16 ± 0.18 |
3.07 |
3.35 |
3.63 |
4.24 |
4.62 |
5.00 |
|
— |
47.63 ± 0.20 |
3.22 |
3.51 |
3.78 |
4.45 |
4.83 |
5.21 |
|
11/2 |
48.30 ± 0.020 |
3.22 |
3.51 |
3.78 |
4.45 |
4.83 |
5.21 |
|
2 |
60.33 ± 0.25 |
3.43 |
3.73 |
4.04 |
4.85 |
5.28 |
5.72 |
|
3 |
88.90 ± 0.38 |
4.80 |
5.23 |
5.66 |
6.66 |
7.26 |
7.87 |
|
4 |
114.30 ± 0.43 |
5.26 |
5.74 |
6.22 |
7.49 |
8.18 |
8.87 |
|
6 |
168.28 ± 0.76 |
6.22 |
9.32 |
7.34 |
9.60 |
10.47 |
11.33 |
|
8 |
219.08 ± 1.02 |
7.16 |
7.82 |
8.48 |
11.13 |
12.14 |
13.16 |
|
10 |
273.05 ± 1.27 |
8.10 |
8.84 |
9.58 |
13.21 |
14.40 |
15.60 |
1.4 The values stated in inch-pound units are to be regarded as standard. The values given in parentheses are mathematical conversions to SI units that are provided for information only and are not considered standard.
1.5 The following precautionary caveat pertains only to the test method portion, Sections 6, 12, and 13, of this specification: This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use.
|
Standard Practice for Ultrasonic Testing of Metal Pipe and Tubing |
|
|
Standard Test Methods and Practices for Chemical Analysis of Steel Products |
|
|
Standard Specification for General Requirements for Specialized Carbon and Alloy Steel Pipe |
|
|
Standard Test Methods and Definitions for Mechanical Testing of Steel Products |
|
|
Standard Specification for Pipe, Steel, Black and Hot-Dipped, Zinc-Coated, Welded and Seamless |
|
|
Standard Practice for Flux Leakage Examination of Ferromagnetic Steel Tubular Products |
|
|
Standard Practice for Eddy Current Examination of Steel Tubular Products Using Magnetic Saturation |
|
|
Standard Practice for Ultrasonic Testing of the Weld Zone of Welded Pipe and Tubing |