ASTM C622-84(1995)
Standard Test Method for Corrosion Resistance of Refractories to Molten Glass Using the Basin Furnace (Withdrawn 2000)
STANDARD published on 1.1.1995
The information about the standard:
Designation standards: ASTM C622-84(1995)
Note: WITHDRAWN
Publication date standards: 1.1.1995
SKU: NS-14306
The number of pages: 4
Approximate weight : 12 g (0.03 lbs)
Country: American technical standard
Category: Technical standards ASTM
Annotation of standard text ASTM C622-84(1995) :
Keywords:
Basin furnace method, Corrosion-refractories, Furnaces, Glass-refractories, Molten glass, Refractories (glass), Simulated service test, corrosion resistance of refractories to molten glass, using the basin, furnace, simulated service test, ICS Number Code 81.080 (Refractories)
Additional information
| 1. Scope |
|
1.1 This test method measures the attack on refractories by molten glass under conditions intended to simulate glass-contact service by exposing one face of the refractory to be tested to molten glass while a temperature gradient is maintained through the refractory. Note 1-Since the test method is intended primarily for soda-lime-silica glasses, some modification of the conditions, procedure, or apparatus may be required for other compositional systems.1.2 This standard may involve hazardous materials, operations, and equipment. This standard does not purport to address all of the safety problems associated with its use. It is the responsibility of the user of this standard to establish appropriate safety and health practices and determine the applicability of regulatory limitations prior to use. |
We recommend:
Technical standards updating
Do you want to make sure you use only the valid technical standards?
We can offer you a solution which will provide you a monthly overview concerning the updating of standards which you use.
Would you like to know more? Look at this page.