ASTM D6941-19

5.1 Fluidization segregation can cause vertical segregation within bins used to hold and transport powders. This can affect product quality or subsequent processes in industrial applications.

5.2 By measuring a powder's segregation tendency, one can compare results to other powders with known history, or determine if the given powder may have a tendency to segregate in a given process.

5.3 Fine powders generally have a lower permeability than coarse bulk solids and therefore tend to retain air longer. Thus, when a bin is filled with a fluidizable powder, the coarser particles settle or are driven into the bed while the finer particles remain fluidized near the surface.

5.4 Fluidization, which serves as a driving force for this mechanism of segregation, is likely to occur when fine powders are pneumatically conveyed into a bin, the bin is filled or discharged at high rates, or if sufficient air flow counter to the flow of powder is present within the bin.

1.1 This practice covers an apparatus and procedure for creating several specimens of a powder sample that, if the powder is one that segregates by the fluidization mechanism, should be different from one another.

1.2 A powder sample is fluidized then, after the fluidizing gas is turned off, it is separated into three or more specimens that can be analyzed for parameters of interest. The difference in these parameters between the specimens is an indication of the segregation potential of the powder.

1.3 Powders must be capable of being fluidized in order to be tested by this practice.

1.4 Temperature- and moisture-sensitive powders may need to be tested at different temperatures and moisture contents, as would happen in an industrial environment.

1.5 This standard is not applicable to all bulk solids and segregation mechanisms: while fluidization is a common segregation mechanism experienced by many fine powders, other segregation mechanisms not evaluated by this standard might induce segregation in practice. Practice D6940 covers another common mechanism: sifting.

1.6 The extent to which segregation will occur in an industrial situation is not only a function of the powder and its tendency to segregate, but also the handling equipment (for example, bin design), process (for example, transfer rates), and environment.

1.7 The values stated in SI units are to be regarded as standard. No other units of measurement are included in this standard.

1.8 This practice offers a set of instructions for performing one or more specific operations. This document cannot replace education or experience and should be used in conjunction with professional judgment. Not all aspects of this practice may be applicable in all circumstances. This ASTM standard is not intended to represent or replace the standard of care by which the adequacy of a given professional service must be judged, nor should this document be applied without consideration of a project’s many unique aspects. The word Standard in the title of this document means only that the document has been approved through the ASTM consensus process.

1.9 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.10 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.