Superconductivity - Part 9: Measurements for bulk high temperature superconductors - Trapped flux density of large grain oxide superconductors
STANDARD published on 21.4.2005
The information about the standard:
Designation standards: IEC 61788-9-ed.1.0
Publication date standards: 21.4.2005
SKU: NS-413743
The number of pages: 39
Approximate weight : 117 g (0.26 lbs)
Country: International technical standard
Category: Technical standards IEC
The category - similar standards:
Measurement of electrical and magnetic quantitiesConducting materials
Annotation of standard text IEC 61788-9-ed.1.0 :
Specifies a test method for the determination of the trapped field (trapped flux density) of bulk high temperature superconductors. This International Standard is applicable to large grain bulk oxide superconductors that have well defined shapes such as round discs, rectangular, and hexagonal pellets. The trapped flux density can be assessed at temperatures from 4,2 K to 90 K. For the purpose of standardization, the trapped flux density will be reported for liquid nitrogen temperature. Specifie une methode dessai pour la determination du champ residuel (densite de flux residuel) des supraconducteurs haute temperature massifs. La presente Norme internationale sapplique aux oxydes supraconducteurs a gros grains ayant des formes bien definies telles que les disques et les pastilles rectangulaires et hexagonales. La densite de flux residuel peut etre determinee pour des temperatures comprises entre 4,2 K et 90 K. Pour les besoins de la normalisation, la densite de flux residuel sera consignee pour la temperature de lazote liquide.
We recommend:
Technical standards updating
Do you want to make sure you use only the valid technical standards?
We can offer you a solution which will provide you a monthly overview concerning the updating of standards which you use.
Would you like to know more? Look at this page.